<-----  向左滑动显示详细信息

产品名称：耐诺碳化钨珠NanorWC
产品型号：NanorWC

---

耐诺碳化钨珠Cemented Carbide Beads（NanorWC）

●概   述：耐诺碳化钨珠NanorWC由全球领先的的滴定滚动工艺成型，在真空电炉中无氧烧结而成。致

密的晶相结构造就了珠子至高的密度和耐磨性，是研磨介质微珠行业革命性的创造。

●Description:

NanorWC cemented carbide bead is shaped with cutting edge dropping

& rolling method from DURA and is sintered in the vacuum kiln. The

compact microstructure of bead offer the bead the highest density and

wear resistance. It is a creative invention of grinding media special

in small sizes.       

●特   点：

★至高的密度：>14.0kg/dm³；

★超高的硬度：>1500kg/mm²；

★稳定性佳：耐酸碱，耐高温。

●Features:

—Highest density: >14.0kg/dm³ ,

—Super hardness: >1500kg/mm², 

—Super stability: acid & alkali resistance, high temperature

resistance .

●应用领域：

★超硬材料的研磨：氧化铝、氮化硼、碳化硅、氮化硅和碳化钨等材料；

★纳米行业：高密度的碳化钨微珠能完成高效的能量的传递，保证物料无污染的纳米级研磨。

●Applications：

—For high hard material grinding: alumina, boron nitride, silicon nitride, silicon

  carbide, tungsten carbide and other material.

—Nano-grinding and dispersion: higher energy transmit of small sizes of NanorWC bead guarantee

  nanometer grinding in free contamination.  

●化学组成 Chemical Composition：

成  分	WC	Co
Wt%	≈85%	≈15%

●物理性质 Typical Properties：

比    重 Specific Gravity	散    重 Bulk Density	莫氏硬度 Hardness Mohs	维 氏 硬 度 Hardness Vickers	耐压强度 Crushing Strength	断裂韧性 Fracture Toughness	弹性模量 Elasticity Module
≥14.3kg/dm3	≥8.5kg/L	9.5	>1500kg/mm2	>220kgf(2mm)	> 15MPa.m1/2	>710GPa/2

●规    格 Sizes：

型号 Code	粒径（φmm） sizes		型号 Code	粒径（φmm） Sizes
NW2	0.2		NW8	0.8～1.0
NW3	0.3		NW10	1.0～1.2
NW4	0.4		NW12	1.2～1.4
NW5	0.4～0.6		NW14	1.4～1.6
NW6	0.6～0.8		NW16	1.6～1.8